Title: | INVESTIGATION ON THE AGING BEHAVIOUR OF THE FUNCTIONALLY GRADIENT MATERIAL CONSISTING OF BORON CARBIDE AND AN ALUMINUM ALLOY | Authors: | Sarıkan, Bertan Balcı, Erhan Übeyli, Mustafa Camuşcu, Necip |
Keywords: | metallic materials inorganic materials aging three-point bending test |
Publisher: | Inst Za Kovinske Materiale I In Tehnologie | Abstract: | In the current study the effect of different temperatures on the aging behaviour of a functionally gradient material was investigated to observe the variation of hardness with respect to the aging time. To do this, the functionally-gradient-material (FGM) specimens, containing boron carbide and aluminum alloy, were produced with hot pressing. Three different layers were used in the FGM samples. Then the macro and micro examinations were carried out to observe the interface between the layers, the porosity, the grain size and probable cracks in these samples. After that the specimens were solutionized at 470 degrees C for I h. Next, the artificial aging at 100 degrees C, 120 degrees C and 150 degrees C was applied to the FGM specimens for 96 h. During the aging treatment, the Brinell hardness measurements were made on the samples at certain intervals. Moreover, three-point bending tests were also carried out to clarify the influence of the aging treatment on the strength of the FGM. Experimental results indicated that the highest hardness values were obtained at 120 degrees C after the aging period of 48-65 h. The aged specimens exhibited higher bending strength than the solutionized specimens. | URI: | https://hdl.handle.net/20.500.11851/6939 | ISSN: | 1580-2949 1580-3414 |
Appears in Collections: | Elektrik ve Elektronik Mühendisliği Bölümü / Department of Electrical & Electronics Engineering Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection |
Show full item record
CORE Recommender
WEB OF SCIENCETM
Citations
5
checked on Sep 7, 2024
Page view(s)
62
checked on Sep 9, 2024
Google ScholarTM
Check
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.